May. 29, 2024
Zirconia ceramic foam filters are used to melt all types of steel such as non-alloy, low alloy, stainless steel and high alloy.
Filters are especially recommended for alloys of high quality grades.
They have good resistance to attack and corrosion of liquid steel, can effectively remove inclusions in liquid metal, reduce trapped gas in liquid metal, and provide laminar flow, so that the filtered metal is significantly clean. Cleaner metals lead to higher quality castings, less scrap and fewer inclusion defects. They are the best choice for filtering of determined for filtering of steel and steel alloys up to the temperature of 1700℃.
Today, a 20GP container of Zirconia Ceramic Foam Filters are delivered To USA after a trial order some days ago.
Technical Data Sheet
| Type | Zirconia ceramic foam filter for steel and high alloy |
| Color | Yellow |
| ZrO2(%) | 85-90 |
| Al2O3 (%) | 5-10 |
| SiO2(%) | ≤4 |
| MgO(%) | 4-5 |
| Porosity | 80-90% |
| Bulk Density | 0.8-1.5g/cm3 |
| Compressive strength | ≥1.5Mpa(Room temperature) |
| PPI | 10-40PPI(PPI=pores per inch) |
| Work Temperature | ≤1700℃ |
| Thermal shock resistance (Times/1100°C) | 6 |
| Certificate | ISO9001:2015 |
| REACH & RoHS |
Why use TF Combo Bags during aluminum casting
Dec. 20, 2024
Dia500mmx30mm 50ppi SIC Ceramic foam filters package
Dec. 19, 2024
Contact Us
+86 158 3011 4065
Guoruiyuan Building, ShengLi North Street, Chang'An District, Shijiazhuang City, Hebei Province, China.
Navigation
Navigation